| DOW Polypropylene H700-12 |
| Dow Plastics - Polypropylene Homopolymer |
| General Information | |
| Product Description | |
|
DOW H700-12 PolyPropylene Resin is intended for use in injection molding processes and is particularly suited for rigid packaging. This product is UL listed. | |
| General | |
| Material Status |
|
| Availability |
|
| Test Standards Available |
|
| Forms |
|
| Processing Method |
|
| ASTM and ISO Properties 1 | |||
| Physical |
Nominal Value |
Unit |
Test Method |
| Density -Specific Gravity |
0.902 |
sp gr 23/23°C |
ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) |
12.0 |
g/10 min |
ASTM D1238 |
| Mechanical |
Nominal Value |
Unit |
Test Method |
| Tensile Strength @ Yield 2 |
4800 |
psi |
ASTM D638 |
| Tensile Elongation @ Yld 2 |
10 |
% |
ASTM D638 |
| Flexural Modulus 3 |
1%
Secant: 210000 |
psi |
ASTM D790 |
| Impact |
Nominal Value |
Unit |
Test Method |
| Notched Izod Impact (73 °F, 0.125 in) |
0.800 |
ft-lb/in |
ASTM D256 |
| Thermal |
Nominal Value |
Unit |
Test Method |
| DTUL @66psi - Unannealed |
203 |
°F |
ASTM D648 |
| Melting Point |
324 |
°F |
DSC |
| CAMPUS® Properties 4 | |||
| Rheological properties |
Nominal Value |
Unit |
Test Method |
| Melt volume-flow rate (230°C/2.16 kg) |
1.10 |
in³/10min |
ISO 1133 |
| Mechanical properties 23°C/50%r.h. |
Nominal Value |
Unit |
Test Method |
| Tensile modulus |
189000 |
psi |
ISO 527-1, -2 |
| Yield stress |
4790 |
psi |
ISO 527-1, -2 |
| Yield strain |
10 |
% |
ISO 527-1, -2 |
| Nominal strain at break |
> 50.0 |
% |
ISO 527-1, -2 |
| Charpy impact strength (+23°C) |
47.6 |
ft-lb/in² |
ISO 179 /1eU |
| Charpy impact strength (-30°C) |
6.19 |
ft-lb/in² |
ISO 179 /1eU |
| Charpy notched impact strength (+23°C) |
0.476 |
ft-lb/in² |
ISO 179 /1eA |
| Charpy notched impact strength (-30°C) |
0.476 |
ft-lb/in² |
ISO 179 /1eA |
| Thermal properties |
Nominal Value |
Unit |
Test Method |
| Temp. of deflection under load (1.80 MPa) |
131 |
°F |
ISO 75-1, -2 |
| Temp. of deflection under load (0.45 MPa) |
198 |
°F |
ISO 75-1, -2 |
| Vicat softening temperature (50°C/h 50N) |
199 |
°F |
ISO 306 |
| Coeff.of linear therm. expansion (parallel) |
0.000066 |
in/in/°F |
ISO 11359-1, -2 |
| Other properties |
Nominal Value |
Unit |
Test Method |
| Density |
0.0327 |
lb/in³ |
ISO 1183 |
| Test specimen production |
Nominal Value |
Unit |
Test Method |
| Processing conditions acc. ISO |
ISO 1873-2 |
|
|
| Injection Molding, melt temperature |
446 |
°F |
ISO 294 |
| Injection Molding, mold temperature |
104 |
°F |
ISO 10724 |
| Injection Molding, injection velocity |
8 |
in/sec |
ISO 294 |
| Notes | |
| 1 | Typical properties: these are not to be construed as specifications. |
| 2 | 2 in/min, 0.125 in |
| 3 | 0.125 in |
| 4 | Typical properties: these are not to be construed as specifications. Additional CAMPUS® data and disclaimer information may be found on CAMPUS® Data Sheet. |
|
Makes no representation or warranty of any kind, express or implied, with respect to this product, as to merchantability, Fitness for particular purpose or otherwise. The data listed represents average values and are believed to be reliable, They are given for information; no guarantee of their accuracy is made, however, and the product is sold upon condition that purchasers shall make their own test to determinate the characteristics of the product and the suitability of the product for their particular process. |