| PULSE™ 2000 |
| Dow Plastics - Acrylonitrile Butadiene Styrene + PC |
| General Information | |
| General | |
| Material Status |
|
| Availability |
|
| Test Standards Available |
|
| Forms |
|
| Processing Method |
|
| ASTM and ISO Properties 1 | |||
| Physical |
Nominal Value |
Unit |
Test Method |
| Density -Specific Gravity |
1.13 |
sp gr 23/23°C |
ASTM D792 |
| Density |
1.13 |
g/cm³ |
ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/3.8 kg) |
7.00 |
g/10 min |
ASTM D1238 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
|
(230°C/3.8 kg) |
2.5 |
g/10 min |
|
|
(260°C/3.8 kg) |
7.0 |
g/10 min |
|
| Mold Shrink, Linear-Flow |
0.0060 |
in/in |
ASTM D955 |
| Molding Shrinkage |
0.60 |
% |
ISO 294-4 |
| Water Absorption @ 24 hrs |
0.15 |
% |
ASTM D570 |
| Water Absorption 24h/23C |
0.15 |
% |
ISO 62 |
| Mechanical |
Nominal Value |
Unit |
Test Method |
| Tensile Modulus |
330000 |
psi |
ASTM D638 |
| Tensile Modulus |
363000 |
psi |
ISO 527-1, -2 |
| Tensile Strength @ Yield 2 |
7700 |
psi |
ASTM D638 |
| Tensile Stress at Yield |
7690 |
psi |
ISO 527-1, -2 |
| Tensile Strength @ Break 2 |
7900 |
psi |
ASTM D638 |
| Tensile Elongation @ Yld 2 |
5.0 |
% |
ASTM D638 |
| Tensile Strain at Yield |
4.5 |
% |
ISO 527-1, -2 |
| Tensile Elongation @ Brk 2 |
130 |
% |
ASTM D638 |
| Tensile Strain at Break |
80 |
% |
ISO 527-1, -2 |
| Flexural Modulus |
340000 |
psi |
ASTM D790 |
| Flexural Modulus |
344000 |
psi |
ISO 178 |
| Flexural Strength @ Yield |
12200 |
psi |
ASTM D790 |
| Impact |
Nominal Value |
Unit |
Test Method |
| Notched Izod Impact 3 | ASTM D256 | ||
|
(-20 °F, 0.125 in)
|
10.0 |
ft-lb/in |
|
|
(73 °F, 0.125 in)
|
12.0 |
ft-lb/in |
|
| Notched Izod Impact Strength | ISO 180 | ||
|
(-40 °F) |
11.4 |
ft-lb/in² |
|
|
(-22 °F) |
17.1 |
ft-lb/in² |
|
|
(73 °F) |
23.8 |
ft-lb/in² |
|
| Instrumented Dart Impact 4 | ASTM D3763 | ||
|
(-20 °F, 0.125 in)
|
Total
Energy: 600 |
in-lb |
|
|
(73 °F, 0.125 in)
|
Total
Energy: 550 |
in-lb |
|
| Thermal |
Nominal Value |
Unit |
Test Method |
| DTUL @66psi - Unannealed (0.125 in) |
265 |
°F |
ASTM D648 |
| HDT B (0.45 MPa) Unannealed |
268 |
°F |
ISO 75B-1, -2 |
| DTUL @264psi - Unannealed (0.125 in) |
230 |
°F |
ASTM D648 |
| HDT A (1.80 MPa) Unannealed |
228 |
°F |
ISO 75A-1, -2 |
| Vicat Softening Point |
290 |
°F |
ASTM D1525 |
| Vicat Softening Temperature | ISO 306 | ||
|
(A120 (120°C/h 10N))
|
291 |
°F |
|
|
(B50 (50°C/h 50N))
|
266 |
°F |
|
| CLTE, Flow (-40 to 180°F (-40 to 82°C)) |
0.000041 |
in/in/°F |
ASTM D696 |
| CAMPUS® Properties 5 | |||
| Rheological properties |
Nominal Value |
Unit |
Test Method |
| Melt volume-flow rate (230°C/3.8 kg) |
0.122 |
in³/10min |
ISO 1133 |
| Mechanical properties 23°C/50%r.h. |
Nominal Value |
Unit |
Test Method |
| Tensile modulus |
342000 |
psi |
ISO 527-1, -2 |
| Yield stress |
7540 |
psi |
ISO 527-1, -2 |
| Yield strain |
5.0 |
% |
ISO 527-1, -2 |
| Nominal strain at break |
> 50.0 |
% |
ISO 527-1, -2 |
| Charpy impact strength (+23°C) |
No Break |
ft-lb/in² |
ISO 179 /1eU |
| Charpy impact strength (-30°C) |
No Break |
ft-lb/in² |
ISO 179 /1eU |
| Charpy notched impact strength (+23°C) |
21.4 |
ft-lb/in² |
ISO 179 /1eA |
| Charpy notched impact strength (-30°C) |
2.38 |
ft-lb/in² |
ISO 179 /1eA |
| Thermal properties |
Nominal Value |
Unit |
Test Method |
| Temp. of deflection under load (1.80 MPa) |
225 |
°F |
ISO 75-1, -2 |
| Temp. of deflection under load (0.45 MPa) |
266 |
°F |
ISO 75-1, -2 |
| Vicat softening temperature (50°C/h 50N) |
266 |
°F |
ISO 306 |
| Coeff.of linear therm. expansion (parallel) |
0.000040 |
in/in/°F |
ISO 11359-1, -2 |
| Other properties |
Nominal Value |
Unit |
Test Method |
| Density |
0.0410 |
lb/in³ |
ISO 1183 |
| Test specimen production |
Nominal Value |
Unit |
Test Method |
| Injection Molding, melt temperature |
518 |
°F |
ISO 294 |
| Injection Molding, mold temperature |
158 |
°F |
ISO 10724 |
| Injection Molding, injection velocity |
8 |
in/sec |
ISO 294 |
| Notes | |
| 1 | Typical properties: these are not to be construed as specifications. |
| 2 | Type I, 2 in/min |
| 3 | Notch Depth: 10 mil |
| 4 | 8000 in/min |
| 5 | Typical properties: these are not to be construed as specifications. Additional CAMPUS® data and disclaimer information may be found on CAMPUS® Data Sheet. |
|
Makes no representation or warranty of any kind, express or implied, with respect to this product, as to merchantability, Fitness for particular purpose or otherwise. The data listed represents average values and are believed to be reliable, They are given for information; no guarantee of their accuracy is made, however, and the product is sold upon condition that purchasers shall make their own test to determinate the characteristics of the product and the suitability of the product for their particular process. |